Low viscosity, clear casting epoxy
PC 510 is a transparent, unfilled epoxy with low viscosity. It is used where a clear material is required. PC 510 can use different curing agents for different applications.
| Properties - Uncured | PC 510 | Part B | Part B-1 |
| Color, visual ......... | Clear | ||
| Viscosity, ASTM-D-2393 (c.p.s. @ 25o C) | 35,000 | ||
| Specific Gravity ............. | 1.70 | ||
| Mix Ratio (weight) | 100:10 | 100:40 | |
| Mixed Viscosity, ASTM-D-2393 (@ 25o C) | 16,000 cps | 600 cps | |
| Pot Life @ 25OC (100 grams) ..... | 5 hrs | 60 min | |
| Shelf Life @ 70o F .......... | 12 months minimum | ||
| Properties - Cured | ||
| Hardness, ASTM-D-2240 (Durometer)...... | Shore D 82 | Shore D 85 |
| Tensile Strength, ASTM-D-638 ....... | 13,000 psi | 6,500 psi |
| Tensile Elongation, ASTM-D-638 ...... | 3.5 % | 5 % |
| Compressive Strength, ASTM-D-695 ....... | 16,500 psi | 15,500 psi |
| Heat Deflection Temperature......... | 150oC | 70oC |
| Service Temperature.............. | 150°C | 105°C |
| Volume Resistivity, ASTM-D-257 (ohm-cm) ... | 0.8 | 1.5 x 1015 |
| Thermal Conductivity (BTU)........ | 8 | |
| Shrinkage (in/in)............. | 0.0005 | |
| Moisture Absorption (% 7days)........ |
1. Weigh out required amount of PC 510 and add the required amount of catalyst.
2. Mix curing agent in thoroughly.
3. Evacuate for 2 - 5 minutes if void-free castings are required.
4. Pour into cavity or mold.
Part B - Cure at room temperature for 4- 8 hours and post cure 1-2 hours at 75°C.
Part B1 - Cure overnight at room temperature (25°C).